Product Description:
A high tack, high shear acrylic adhesive film coated 2.0 mils on both sides of a high quality polyester film.
Product Use:
Developed primarily for Low Surface Energy (LSE) bonding.
Typical Applications include;
- Bonding foam to rigid and flexible plastics
- Laminating and mounting to many low-surface energy materials
- Excellent foam bonding properties
- Low VOC bonding applications
Benefits of the high performance LSE Acrylic adhesive:
- Low fogging, low flammability
- High tack and shear properties
- Excellent bond to variety of foam substrates
Adhesive Family
750 High Performance Acrylic Adhesive Adhesive System for LSE bonding
Release Liner
74# White Polycoated Kraft
Carrier/Backing
1/2 mil Clear Polyester Film
Tape Construction
Double Coated PET Film Tape
Adhesive Liner Side
Acrylic
Adhesive Thickness - Liner Side (Mils)
2.0
Adhesive Exposed Side
Acrylic
Adhesive Thickness - Exposed Side (Mils)
2.0
Peel Exposed Side
77
Oz/Inch
Note: Typical Values per PSTC #101 Method E, Backed with 1 Mil PET. 72 Hour Dwell.
Peel Liner Side
77
Oz/Inch
Note: Typical Values per PSTC #101 Method E, Backed with 1 Mil PET. 72 Hour Dwell.
Shear Exposed Side
9
days
Note: Typical Values per PSTC #107 Procedure A Modified, 1000 grams/Sq.Inch @ 72oF. No Dwell.
Shear Liner Side
9
days
Note: Typical Values per PSTC #107 Procedure A Modified, 1000 grams/Sq.Inch @ 72oF. No Dwell.
Service Temperature
-30
°F to
250
°F
Note: Data is based on limited testing and under no load.
Roll Weight
Note: Theoretical number only. The actual roll weight may vary.
Tape Thickness (without release liner)
4.5 mils
Note: Theoretical number only. Does not include Release Liner. The actual Tape thickness may vary.
SDS Note: If the specific product is not listed in the appendix of the provided "Article Exemption Letter", please contact your sales/account representative for a SDS.
Bonding Study Results
Manufacturer |
Material Description | Bonding Result | Notes/Comments |